ASTM B733-15 pdf free download.Standard Specification for Autocatalytic (Electroless) Nickel-Phosphorus Coatings on Metal.
1.1 This specification covers requirements thr autocatalytic (electroless) nickel-phosphorus coatings applied from aqueous solutions to metallic products fur engineering (functional) uses.
1.2 The coatings are alloys of nickel and phosphorus produced by autocatalytic chemical reduction with hypophosphite. Because the deposited nickel alloy is a catalyst for the reaction, the process is self-sustaining. The chemical and physical properties of the deposit vary primarily with its phosphorus content and subsequent heat treatment. The chemical makeup of the plating solution and the use of the solution can affect the porosity and corrosion resistance of the deposit. For more details, see ASTM STP 265 (1)2 and Refs (2) (3) (4) and (5).
1.3 The coatings are generally deposited from acidic solu(ions operating at elevated temperatures.
1.4 The process produces coatings of uniform thickness on irregularly shaped parts, provided the plating solution circulates freely over their surfaces.
1.5 The coatings have multifunctional properties, such as hardness, heat hardenability, abrasion, wear and corrosion resistance, magnetics. electrical conductivity provide diffusion barrier, and solderability. They are also used for the salvage of worn or mismachined parts.
1.6 The low phosphorus (2 to 4 % P) coatings are microcrystalline and possess high as-plated hardness (620 to 750 FIK 100). These coatings are used in applications requiring abrasion and wear resistance.
1.7 Lower phosphorus deposits in the range between 1 and 3 % phosphorus are also microcrystalline. These coatings are used in electronic applications providing solderahility,bondability. increased electrical conductivity, and resistance to strong alkali solutions.
1.8 The medium phosphorous coatings (5 to 9 % P) are most widely used to meet the general purpose requirements of wear and corrosion resistance.
1.9 The high phosphorous (more than 10 % P) coatings have superior salt-spray and acid resistance in a wide range of applications. They are used on beryllium and titanium parts for low stress properties. Coatings with phosphorus contents greater than 11.2 % P are not considered to be ferromagnetic.ASTM B733 pdf download.